High Qulality PVC Resin SG5 for Pipe and Food Package CAS NO.9002-86-2
- FOB Price: USD: 1,300.00-1,330.00 /Metric Ton Get Latest Price
- Min.Order: 13 Metric Ton
- Payment Terms: L/C,D/P,T/T
- Available Specifications:
1(13-26)Metric Ton1(26-104)Metric Ton
- Product Details
Keywords
- Polyvinylchlorid Resin
- PVC Pipe
- SG5
Quick Details
- ProName: High Qulality PVC Resin SG5 for Pipe a...
- CasNo: 9002-86-2
- Molecular Formula: -[CH2CHCl]-n
- Appearance: powder
- Application: pipe,frpfile,cling film,food package,p...
- DeliveryTime: 20 days
- PackAge: 25kgs bag,jumbo bag
- Port: Qingdao
- ProductionCapacity: 100 Metric Ton/Day
- Purity: 99%
- Storage: dry place
- Transportation: Ocean
- LimitNum: 13 Metric Ton
- Grade: Industrial Grade,Food Grade
- K value: 67
- whiteness: 75
- packing: 25kgs bag
Superiority
PVC Resin
Introduction:
Polyvinyl chloride has the outstanding characteristics of abundant raw materials (oil, limestone, coke, salt and natural gas), mature manufacturing process, low price, and wide range of uses. It has become the second largest general-purpose resin in the world after polyethylene resin. 29% of the world's total synthetic resin consumption. Polyvinyl chloride is easy to process and can be processed by molding, laminating, injection molding, extrusion, calendering, blow molding, etc. Polyvinyl chloride is mainly used to produce soft plastic products such as artificial leather, films, and wire sheaths, as well as hard plastic products such as plates, doors and windows, pipes and valves. Polyvinyl chloride is flame-retardant (flame retardant value above 40), high chemical resistance (resistant to concentrated hydrochloric acid, 90% sulfuric acid, 60% nitric acid and 20% sodium hydroxide), mechanical strength And the advantages of good electrical insulation. But its heat resistance is poor, with a softening point of 80°C, it starts to decompose and change color at 130°C, and precipitate HCI.
Application and usage:
Semirigid products,
Medical film,
Sheets,
Tubes,
Artificial leathers,
Rigid profiles,
Electric cables,
Calendaring and extruding products
Details
PVC RESIN
Polyvinyl chloride has the outstanding characteristics of abundant raw materials (oil, limestone, coke, salt and natural gas), mature manufacturing process, low price, and wide range of uses. It has become the second largest general-purpose resin in the world after polyethylene resin. 29% of the world's total synthetic resin consumption. Polyvinyl chloride is easy to process and can be processed by molding, laminating, injection molding, extrusion, calendering, blow molding, etc. Polyvinyl chloride is mainly used to produce soft plastic products such as artificial leather, films, and wire sheaths, as well as hard plastic products such as plates, doors and windows, pipes and valves. Polyvinyl chloride is flame-retardant (flame retardant value above 40), high chemical resistance (resistant to concentrated hydrochloric acid, 90% sulfuric acid, 60% nitric acid and 20% sodium hydroxide), mechanical strength And the advantages of good electrical insulation. But its heat resistance is poor, with a softening point of 80°C, it starts to decompose and change color at 130°C, and precipitate HCI.
Application and usage:
Semirigid products,
Medical film,
Sheets,
Tubes,
Artificial leathers,
Rigid profiles,
Electric cables,
Calendaring and extruding products PVC RESIN
Property:
PVC resin: the thermoplastic high-molecular polymer made by the suspension polymerization of vinyl chloride monomer. The molecular formula :- (CH2 - CHCl) n - (N: degree of polymerization, N= 590 ~ 1500)
Application: Automobile interiors, family decorative materials, advertising light box, shoe soles, PVC
pipes, PVC profiles, PVC sheet and plate, rolling film, inflatable toys, outdoor products, PVC wire and cable, PVC artificial leather, wood and plastic floor, corrugated board, etc.
Qualtiy: GB/T 5761-2006 Standard
|
SG1 |
SG2 |
SG3 |
SG4 |
SG5 |
SG6 |
SG7 |
SG8 |
|
Viscosity, ml/g(or K value) |
156-144 (72-71) |
143-136 (74-73) |
135-127 (72-71) 1350-1250 |
126-119 (70-69) 1250-1150 |
118-107 (68-66) 1100-1000 |
106-96 (65-63) 950-850 |
95-87 (62-60) 850-750 |
86-73 (59-55) 750-650 |
|
Number of impurity particle≤ Число примесных частиц, не более |
30 |
30
|
30
|
30 |
30 |
30 |
40 |
40 |
|
Volatiles content %,≤
|
0.40 |
0.40 |
0.40 |
0.40 |
0.40 |
0.40 |
0.40 |
0.40 |
|
Appearing density g/ml≥
|
0.42 |
0.42 |
0.42 |
0.45 |
0.45 |
0.45 |
0.45 |
0.45 |
|
residue after sieve
|
0.25mm ≦ |
2.0 |
2.0 |
2.0 |
2.0 |
2.0 |
2.0 |
2.0 |
2.0 |
0.063mm ≥ |
90 |
90 |
90 |
90 |
90 |
90 |
90 |
90 |
|
Number of grain/400cm2≤
|
40 |
40 |
40 |
40 |
40 |
40 |
50 |
50 |
|
Plasticizer absorbency value of 100g resin g≥ |
25 |
25 |
25 |
22 |
17 |
15 |
- |
- |
|
Whiteness %,≥ |
75 |
75 |
75 |
75 |
75 |
75 |
70 |
70 |
|
Water extractant solution conductivity, 【us/(cm.g)】≤ |
5 |
5 |
5 |
- |
- |
- |
- |
- |
|
Residual chlore thylene content mg/kg≤ |
10 |
10 |
10 |
10 |
10 |
10 |
10 |
10 |
|
Residual Ethyidenedichlorideug/g |
150 |
150 |
150 |
150 |
150 |
150 |
150 |
150 |